MSDS Sheets - ABS

Technical Data

Acrylonitrile Butadiene Styrene

Physical

Nominal Value Unit

Test Method

Specific Gravity

--

1.05 g/cm3

ASTM D792

23°C

1.05 g/cm3

ISO 1183

Melt Mass-Flow Rate (MFR)

ASTM D1238

200°C/5.0 kg

1.6 g/10 min

220°C/10.0 kg

22 g/10 min

Melt Volume-Flow Rate (MVR) (220°C/10.0 kg)

22.0 cm3/10min

ISO 1133

Mechanical

Nominal Value Unit

Test Method

Tensile Stress

Yield

54.0 MPa

ISO 527-2/50

Break

37.0 MPa

ISO 527-2/50

3.00 mm4

45.1 MPa

ASTM D638

Tensile Elongation

Break, 3.00 mm4

25%

ASTM D638

Break

20%

ISO 527-2/50

Flexural Modulus

6.00 mm5

2650 MPa

ASTM D790

6

2200 MPa

ISO 178

Flexural Strength

6.00 mm5

77.5 MPa

ASTM D790

6

76.0 MPa

ISO 178

Impact

Nominal Value Unit

Test Method

Charpy Notched Impact Strength

20 kJ/m2

ISO 179

Charpy Unnotched Impact Strength

No Break

ISO 179

Notched Izod Impact

23°C, 3.00 mm

210 J/m

ASTM D256

23°C, 6.00 mm

180 J/m

ASTM D256

--

18 kJ/m2

ISO 180/1A

Unnotched Izod Impact Strength

60 kJ/m2

ISO 180/1U

Hardness

Nominal Value Unit

Test Method

Rockwell Hardness (R-Scale)

116

ASTM D785

Ball Indentation Hardness (H 358/30)

110 MPa

ISO 2039-1

Thermal

Nominal Value Unit

Test Method

Deflection Temperature Under Load

1.8 MPa, Unannealed

85.0 °C

ASTM D648

1.8 MPa, Unannealed

88.0 °C

ISO 75-2/A

1.8 MPa, Annealed

95.0 °C

ASTM D648

1.8 MPa, Annealed

98.0 °C

ISO 75-2/A

Vicat Softening Temperature

--

105 °C

ASTM D1525

--

104 °C

ISO 306/A50

--

100 °C

ISO 306/B50

Flammability

Nominal Value Unit

Test Method

Flame Rating (1.60 mm)

HB

UL 94

Injection

Nominal Value Unit

Drying Temperature

80.0 to 85.0 °C

Drying Time

2.0 to 4.0 hr

Rear Temperature

180 to 220 °C

Middle Temperature

190 to 230 °C

Front Temperature

190 to 230 °C

Mold Temperature

30.0 to 70.0 °C