Wood Composite Data Sheet
3D Wood material data sheet |
|||
Main ingredients |
The resin type: |
PLA/PP alloy |
|
Resin content%: |
70~40 |
||
Fiber types: |
Natural plant fiber |
||
Fiber content%: |
10~40 |
||
principal physical properties |
granules |
melt flow velocity g/10min (GB/T 3682-2000): |
(190,5.00)8~20 |
Injection molding sample testing at room temperature are for reference only |
impact strength (Type A gap)KJ/m² (GB/T 1843-2008): |
≥5.0 |
|
bending strength MPa(GB/T9341-2008) |
:≥26.0 |
||
flexural modulus MPa(GB/T9341-2008) |
:≥1200.0 |
||
tensile strength MPa (GB/T1040.1-2006): |
≥18.0 |
||
elasticity modulus MPa (GB/T1040.1-2006): |
≥1200.0 |
||
elongation at break % (GB/T1040.1-2006): |
≥9.0 |
||
shore hardness D(GB/T2411-2008): |
≥70.0 |
||
Density of the sample piece g/cm³ (GB/T 1933-2009): |
≈1.00 |
||
manufacturing technique |
Drawing at room temperature |
Device type: |
/ |
fiber-forming temperature℃: |
165~185 |
||
maximum temperature℃: |
≤190 |
||
|
For equipment performance, temperature above are for reference only, debug temperature to pull out silk smooth surface, no burr, pellet, cross section pore-free is preferred. |